聚乳酸生物降解复合膜向食品模拟物的总迁移及钙的迁移研究

何金凤; 林勤保; 任纪州; 吕新广; 李忠

doi:10.19969/j.fxcsxb.21080602

您当前的位置：

首页 >

文章列表页 >

聚乳酸生物降解复合膜向食品模拟物的总迁移及钙的迁移研究

实验技术与方法 | 更新时间：2023-02-13

- 聚乳酸生物降解复合膜向食品模拟物的总迁移及钙的迁移研究
- Overall Migration and Calcium Migration from Biodegraded Polylactic Acid Composite Films into Food Simulant
- 分析测试学报 2021年40卷第11期页码：1639-1644
- 作者机构：
  
  1.暨南大学包装工程研究所，广东普通高校产品包装与物流重点实验室，广东珠海 519070
  2.武汉轻工大学机械工程学院，湖北武汉 430023
  3.拱北海关技术中心，广东珠海 519000
- 作者简介：
  
  林勤保，博士，研究员，研究方向：食品包装安全，E－mail：7899966@qq.com
- 基金信息：
  
  国家重点研发计划(2018YFC1603204)
- DOI：10.19969/j.fxcsxb.21080602
  中图分类号：
扫描看全文
何金凤,林勤保,任纪州等.聚乳酸生物降解复合膜向食品模拟物的总迁移及钙的迁移研究[J].分析测试学报,2021,40(11):1639-1644.

HE Jin-feng,LIN Qin-bao,REN Ji-zhou,et al.Overall Migration and Calcium Migration from Biodegraded Polylactic Acid Composite Films into Food Simulant[J].Journal of Instrumental Analysis,2021,40(11):1639-1644.
何金凤,林勤保,任纪州等.聚乳酸生物降解复合膜向食品模拟物的总迁移及钙的迁移研究[J].分析测试学报,2021,40(11):1639-1644. DOI： 10.19969/j.fxcsxb.21080602.

HE Jin-feng,LIN Qin-bao,REN Ji-zhou,et al.Overall Migration and Calcium Migration from Biodegraded Polylactic Acid Composite Films into Food Simulant[J].Journal of Instrumental Analysis,2021,40(11):1639-1644. DOI： 10.19969/j.fxcsxb.21080602.

摘要

研究了5种不同碳酸钙含量的PLA/PBAT/CaCO,3,复合膜中的钙在40 ℃和70 ℃下向3%乙酸食品模拟物的迁移及向3种食品模拟物（3%乙酸、10%乙醇、95%乙醇）的总迁移，探究了复合膜中碳酸钙含量与总迁移的关系，并研究了紫外老化处理对迁移的影响。结果表明，5种复合膜向3%乙酸中的总迁移量均超过总迁移限值（OML），且总迁移主要受复合膜中碳酸钙含量的影响，钙浓度与总迁移量呈线性关系。同时，随着复合膜中碳酸钙含量的增加，钙的迁移量增加，且不同碳酸钙含量的复合膜均在短时间内达到迁移平衡（40 ℃，4 h）。将复合膜紫外老化处理较长时间（24 h以上）会导致钙的迁移量减少，可能的原因是紫外照射引起聚己二酸/对苯二甲酸丁二酯（PBAT）的交联反应，从而抑制了钙的迁移。此类生物降解复合膜作为食品接触材料的安全性值得进一步关注和研究。

Abstract

While biodegradable plastics continually exhibit many excellent properties，their safety has been increasingly concerned．In this study，the migration risk of calcium in food contact degradation composite film was evaluated，with polylactic acid（PLA） and polylactic acid/poly（butyleneadipate-co-terephthalate）（PBAT） as the substrates and calcium carbonate （CaCO,3,） as the inorganic filler．The calcium concentrations in five kinds of PLA/PBAT/CaCO,3, composite films with various contents of CaCO,3, were determined by inductively coupled plasma optical emission spectrometry（ICP－OES）．Meanwhile， the PLA/PBAT/CaCO,3, films were characterized by scanning electron microscopy（SEM）．The overall migration of PLA/PBAT/CaCO,3, films into three food simulants（3% acetic acid，10% ethanol，95% ethanol） were investigated，and the relationship between the overall migration results and the calcium content was explored．Migrations of calcium from PLA/PBAT/CaCO,3, films into the acidic food stimulant of 3% acetic acid at 40 ℃/24 h and 70 ℃/2 h were investigated，respectively．Furthermore，effect of ultraviolet aging treatment on the migration was also studied．Results showed that the overall migration of the five composite films into 95% ethanol was higher than that into 10% ethanol，and the overall migration into 3% acetic acid exceeded the overall migration limit（OML），which may lead to food safety risks．The overall migration was mainly affected by CaCO,3,，and the calcium concentration had a linear relationship with the overall migration into 3% acetic acid．With the increase of CaCO,3, content，different degrees of agglomeration occurred on the surface of the films，while the migration of calcium was affected by the agglomeration．For all the composite films with different CaCO,3, contents，the migration equilibriums were obtained in a short time（40 ℃，4 h）．The long time（more than 24 h） UV aging for composite film inhibited the calcium migration due to the cross-linking of PBAT．The safety of these biodegradable composite films as food contact materials is worth further study．

关键词

食品接触材料生物降解薄膜聚乳酸碳酸钙迁移紫外老化

Keywords

food contact materialbio-degradation filmpolylactic acid（PLA）calcium carbonatemigrationultraviolet aging

references

Li Y N，Ren J Z，Wang B H，Lu W Q，Wang H X，Hou W．Int. J. Biol. Macromol.，2020，165（A）：1258－1263.

Hamontree C，Sritham E，Phunsombat P，Chaishome J．MATEC Web of Conferences，Phuket，Thailand，2018．

Zhang Y，Jia S L，Pan H W，Wang L J，Bian J J，Guan Y，Li B H，Zhang H L，Yang H L，Dong L S．Korean J. Chem. Eng.，2021，38（8）：1746－1755.

Zhang T，Zhang C L，Song X Y，Weng Y X．China Plasit. （张婷，张彩丽，宋鑫宇，翁云宣．中国塑料），2021，35（7）：115－125.

Piekarska K，Piorkowska E，Bojda J．Polym. Test.，2017，62：203－209.

Rocha D B，de Carvalho J S，de Oliveira S A，dos Santos Rosa D．J. Appl. Polym. Sci.，2018，135（35）：1－9.

Comission Regulation（EU）No 10/2011 of 14 January 2011 on Plastic Materials and Articles Intended to Come into Contact with Food．

Gu S Y，Zhang K，Ren J，Zhan H．Carbohydr. Polym.，2008，74（1）：79－85.

Iuliano A，Nowacka M，Rybak K，Rzepna M．J. Appl. Polym. Sci.，2019，137（11）：48462.

Stloukal P，Verney V，Commereuc S，Rychly J，Matisova－Rychla L，Pis V，Koutny M．Chemosphere，2012，88（10）：1214－1219.

Kijchavengkul T，Auras R，Rubino M，Alvarado E，Camacho Montero J R，Rosales J M．Polym. Degrad. Stab.，2010，95（2）：99－107.

Zhong H N，Zhang M，He J F，Lin Q B，Li Z K．Sci. Technol. Food Ind. 钟怀宁，张明，何金凤，林勤保，李泽坤．食品工业科技），2019，40（1）：202－208.

Gardette M，Thérias S，Gardette J L，Murariu M，Dubois P．Polym. Degrad. Stab.，2011，96（4）：616－623.

Mucha M，Bialas S，Kaczmarek H．J. Appl. Polym. Sci.，2014，131（8）：40144.

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

纸基包装材料中抗氧化剂及增塑剂向干性食品模拟物Tenax TA迁移的研究

食品及食品接触材料中烃类矿物油分析技术进展

一次性塑料餐具中风险物质的筛查

GC－MS/MS法测定食品接触用硅橡胶制品中6种环硅氧烷迁移量

高效液相色谱－串联质谱法测定食品接触用橡胶奶衬制品中5种化合物的迁移量