Characterization on Copolymer Structure of Ethylene and Methyl Methacrylate by 1H NMR and 13C NMR

您当前的位置：

首页 >

文章列表页 >

Characterization on Copolymer Structure of Ethylene and Methyl Methacrylate by 1H NMR and 13C NMR

- Characterization on Copolymer Structure of Ethylene and Methyl Methacrylate by 1H NMR and 13C NMR
- Vol. 37, Issue 6, Pages: 734-738(2018)
- 作者机构：
  
  1. 华东理工大学材料科学与工程学院
  2. 上海市先进聚合物材料重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC：
扫描看全文
Characterization on Copolymer Structure of Ethylene and Methyl Methacrylate by 1H NMR and 13C NMR. [J]. 37(6):734-738(2018)
DOI：

Characterization on Copolymer Structure of Ethylene and Methyl Methacrylate by 1H NMR and 13C NMR. [J]. 37(6):734-738(2018) DOI：

摘要

采用核磁共振（1H NMR、13C NMR）技术对由双［N-（2,6-二异丙基苯基）-3-异丙基水杨醛亚胺］镍（Ⅱ）配合物/甲基铝氧烷（Methylaluminoxane，MAO）催化乙烯-甲基丙烯酸甲酯共聚得到的共聚物（EMMA-a）的微观结构和组成进行了详细的分析与表征，同时对自由基聚合制得的乙烯-甲基丙烯酸甲酯共聚物（EMMA-b）作了相应的分析与表征。通过1H NMR数据，计算得到两种共聚物样品中共聚单体甲基丙烯酸甲酯（MMA）的插入率分别为14.10%和10.26%（摩尔百分数）。基于13C NMR数据，分析比较了由配位共聚与自由基共聚所得共聚物样品在微观结构上的区别，结果发现，在共聚物的乙烯链段部分，由配位共聚得到的共聚物样品EMMA-a主要含有甲基型支链，而由自由基共聚所得共聚物样品EMMA-b具有长链型支链。另外，在共聚物的MMA链节部分，EMMA-a中的MMA单元的羰基（C‖O）碳的化学位移为177.27，而EMMA-b中的MMA单元的羰基（C‖O）碳的化学位移为175.96。

Abstract

The microstructure and composition of ethylene and methyl methacrylate copolymer（EMMA-a）,obtained with bis ［N-（2,6-diisopropylphenyl）-3-isopropylsalicylaldiminate］ nickel（Ⅱ）/methylaluminoxane（MAO）,were fully characterized by 1H NMR and 13C NMR techniques.The copolymer（EMMA-b） of ethylene and methyl methacrylate,produced by radical polymerization,also experienced the corresponding characterization.According to the 1H NMR data,the corporations of the co-unit MMA in the two copolymers were calculated to be 14.10% and 10.26%,respectively.Based on the 13C NMR data,the microstructures of the two copolymers were compared.The results showed that in the ethylene co-units,methyl type branches mainly appeared in the EMMA-a,while long-chain branches were found in the EMMA-b.Besides,in the MMA co-units,the chemical shift of carbon in carbonyl（C‖O） of EMMA-a was found as 177.27,while the chemical shift of carbon in carbonyl（C‖O） of EMMA-b was 175.96.

关键词

核磁共振（NMR）乙烯-甲基丙烯酸甲酯共聚物（EMMA）微观结构表征

Keywords

nuclear magnetic resonance（NMR）ethylene and methyl methacrylate copolymer（EMMA）microstructurescharacterization

references

Views

656

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Structural Identification of Polyglycerol Fatty Acid Esters

Preparation and Characterization of Layered Perovskite type Organic-Inorganic Hybrids (RNH3)2CuCl4

Synthesis and Characterization of 8-Hydroxyquinoline Ligand and Trigonal bipyramidal Co(Ⅱ) Complex

Synthesis,Characterization and Fluorescent Properties of (E）-2-［2-(4-Methoxyphenyl）ethenyl］-8-acetoxyquinoline

Study of Preparation of Ag Nanoparticles with Vitamin E through Green Chemical Reduction

Related Author

No data

Related Institution

Guangdong Provincial Engineering Research Center for Quality and Safety of Traditional Chinese Medicine，Guangdong Provincial Key Laboratory of Chemical Measurement and Emergency Test Technology， Institute of Analysis，Guangdong Academy of Sciences（China National Analytical Center，）

江汉大学化学与环境工程学院

黄山学院化学化工学院

合肥师范学院化学化工系

辽宁石油化工大学化学化工与环境学部

Address：100 Xianlie Middle Road, Guangzhou Postal code：510070
Tel：020-87684776,37656606 Fax：020-87684776 Email：fxcsxb@china.com
Technical support is provided by Beijing Founder electronics co., LTD 粤ICP备12017312号-3 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰